多功能抗激光损伤高反射膜
赵缨慰;付秀华;李 珊;宫大为
长春理工大学,吉林 长春 130022
摘要

为了能同时满足半导体激光器和YAG激光器对薄膜的特殊要求,在分析高反射膜理论的基础上,选取TiO2和SiO2为高、低折射率材料镀制了周期性多层介质高反射膜。研究了材料的光学及机械特性,重点解决了薄膜的消偏振和抗激光损伤问题。实验采用电子束真空镀膜并加以考夫曼离子源辅助沉积,利用TFC软件进行膜系设计,通过调整镀膜工艺参数和监控方法,在10 mm×1.8 mm的K9基底上镀制了符合要求的高反射膜,结果表明,当激光以45°入射时,薄膜在900~1 100 nm的p光与s光的反射率均大于99.95%。所制备的高反射膜性能稳定,抗激光损伤阈值高,能同时满足两种激光器的使用要求。

关键词 光学薄膜   高反射膜   激光损伤   消偏振  
Anti-laser-induced damage high reflectance film with multifunction
ZHAO Ying-wei;FU Xiu-hua;LI Shan;GONG Da-wei
Changchun University of Science and Technology,Changchun 130022,China
Abstract:

In order to meet the special requirements of semiconductor lasers and YAG lasers for films synchronously, the principles of a high reflectance film were researched. Then, by choosing the TiO2 and SiO2 films as the higher and lower reflectance materials, a high laser-induced damage threshold reflectance film was deposited. The optical and mechanical properties of the materials were investigated and the depolarization and anti-laser-induced damage of the film were overcome. In experiments, the electron beam vacuum coating and the Kaufman ion source assisted technique were used to deposit the film and the TFC software was used to design the thin-film structure. By adjusting the parameters of coating process and monitor method, the high reflectance film was successfully deposited on a 10 mm×1.8 mm K9 substrate. Obtained results show that the both reflectances of p-component and s-component have exceeded 99.95% at the wavelength of 900 nm~1 100 nm when the incidence of laser is 45°. The experiments demonstrate that the high reflectance film has a stable property and a high laser-induced damage threshold, and it is suitable for both semiconductor lasers and YAG lasers.

Keywords: optical thin-film   high reflectance film   laser-induced damage   depolarization  
收稿日期 2010-01-11 修回日期 1900-01-01 网络版发布日期  
基金项目:

通讯作者:
作者简介:
作者Email:

参考文献:
本刊中的类似文章
1.宫大为, 付秀华, 耿似玉, 杨道奇.红外双波段激光滤光膜的研制[J]. 中国光学, 2011,4(3): 293-298
2.卫耀伟, 刘志超, 陈松林.TiO2/Al2O3薄膜的原子层沉积和光学性能分析[J]. 中国光学, 2011,4(2): 188-195

Copyright by 中国光学