LU Xin, TIAN Jian. Preparation and luminescent properties of Yb3+∶Y2O3 ultrafine powders by low-temperature combustion synthesis[J]. Chinese Optics, 2011, 4(6): 667-671.
Citation: LU Xin, TIAN Jian. Preparation and luminescent properties of Yb3+∶Y2O3 ultrafine powders by low-temperature combustion synthesis[J]. Chinese Optics, 2011, 4(6): 667-671.

Preparation and luminescent properties of Yb3+∶Y2O3 ultrafine powders by low-temperature combustion synthesis

  • Received Date: 11 Sep 2011
  • Rev Recd Date: 13 Oct 2011
  • Publish Date: 25 Dec 2011
  • Yb3+∶Y2O3 ultrafine powders were prepared by using the low-temperature combustion synthesis(LCS) with the solutions of mixed nitrates and urea in mol concentration ratio of 3∶1 and at a ignition temperature about 600 ℃. The Yb3+∶Y2O3 ultrafine powders were measured by using a X-ray Diffractometer(XRD), a Scanning Electron Microscope(SEM) and a Fluorescence Spectrometer(FS). The influences of ignition temperature, fuel content and calcination temperature on the characteristics of the powders were investigated. The experimental result shows that the grain diameter of as-prepared powders is about 15-30 nm, and the grain dispersion is good without obvious agglomeration. Moreover the fluorescence performace of the powders is well, and the emission peaks are located at 976, 1 030 and 1 075 nm. As a result, the Yb3+∶Y2O3 ultrafine powders can be propitious to the preparation of Yb3+∶Y2O3 transparent ceramics.

     

  • loading
  • [1] 卢利平,张希艳,柏朝晖,等 . 低温燃烧合成红外响应材料CaS∶Eu,Sm及性能表征[J]. 稀有金属材料与工程 ,2006,35(8):1211-1214. LU L P,ZHANG X Y,BAI ZH H,et al.. Synthesis of IR sensitive material CaS∶Eu,Sm by low-temperature combustion and its characterization[J]. Rare Metal Materials Eng.,2006,35(8):1211-1214.(in Chinese) [2] TAKAICHI K,YAGI H,LU J,et al.. Highly efficient continuous-wave operation at 1 030 and 1 075 nm wavelengths of LD-pumped Yb3+∶Y2O 3 ceramic lasers[J]. Appl. Phys. Lett.,2004,84(3):317-319. [3] LU J,BISSON J F,TAKAICHI K,et al.. Yb3+∶Sc2O3 ceramic laser[J]. Appl. Phys. Lett.,2003,83(6):1101-1103. [4] 张晓顺,翟秀静,邱竹贤,等. 燃烧合成法制备纳米氧化锌[J]. 分子科学学报 ,2005,21(1):12-15. ZHANG X SH,ZHAI X J,QIU ZH X,et al.. The preparation of nanometer zinc oxide by combustion synthesis[J]. J. Molecular Sci.,2005,21(1):12-15.(in Chinese)
  • 加载中

Catalog

    通讯作者: 陈斌, bchen63@163.com
    • 1. 

      沈阳化工大学材料科学与工程学院 沈阳 110142

    1. 本站搜索
    2. 百度学术搜索
    3. 万方数据库搜索
    4. CNKI搜索
    Article views(3008) PDF downloads(1154) Cited by()
    Proportional views

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return